@article {84, title = {Atomic-scale modelling of elastic and failure properties of clays}, journal = {Molecular Physics}, volume = {112}, year = {2014}, month = {May-19-2014}, pages = {1294-1305}, type = {Article}, abstract = {

The elastic and failure properties of a typical clay, illite, are investigated using molecular simulation. We employ a reactive (ReaxFF) and a non-reactive (ClayFF) force field to assess the elastic properties of the clay. As far as failure is concerned, ReaxFF was used throughout the study; however, some calculations were also performed with ClayFF. A crack parallel to the clay layers is found to have low fracture resistance when submitted to a tensile loading perpendicular to the crack. The mechanism of both yield and fracture failures is decohesion in the interlayer space. In contrast, under shear loading, the nanoscale failure mechanism is a stick-slip between clay layers. No fracture propagation is observed as the clay layers slide on top of each other. The low fracture resistance in mode I and the stick-slip failure in mode II are both the consequence of the lack of chemical bonds between clay layers where the cohesion is provided by non-covalent interactions. This work, which provides a description of the failure of clays at the microscopic scale, is the first step towards describing the failure of clays at a larger scale where the polycrystalline distribution of clay grains must be taken into account.

}, keywords = {clay, elastic properties, fracture, reactive molecular simulation}, issn = {0026-8976}, doi = {10.1080/00268976.2014.897393}, author = {Gy{\"o}rgy Hantal and Brochard, Laurent and Hadrien Laubie and Ebrahimi, Davoud and Roland Jean-Marc Pellenq and Franz-Josef Ulm and Benoit A. Coasne} }