@article {679, title = {Multiscale poromechanics of wet cement paste}, journal = {Proceedings of the National Academy of Sciences}, volume = {2}, year = {2019}, month = {May-09-2019}, pages = {201901160}, abstract = {

Capillary effects, such as imbibition drying cycles, impact the mechanics of granular systems over time. A multiscale poromechanics framework was applied to cement paste, which is the most common building material, experiencing broad humidity variations over the lifetime of infrastructure. First, the liquid density distribution at intermediate to high relative humidity is obtained using a lattice gas density functional method together with a realistic nanogranular model of cement hydrates. The calculated adsorption/desorption isotherms and pore size distributions are discussed and compare well with nitrogen and water experiments. The standard method for pore size distribution determination from desorption data is evaluated. Second, the integration of the Korteweg liquid stress field around each cement hydrate particle provided the capillary forces at the nanoscale. The cement mesoscale structure was relaxed under the action of the capillary forces. Local irreversible deformations of the cement nanograins assembly were identified due to liquid\–solid interactions. The spatial correlations of the nonaffine displacements extend to a few tens of nanometers. Third, the Love\–Weber method provided the homogenized liquid stress at the micrometer scale. The homogenization length coincided with the spatial correlation length of nonaffine displacements. Our results on the solid response to capillary stress field suggest that the micrometer-scale texture is not affected by mild drying, while nanoscale irreversible deformations still occur. These results pave the way for understanding capillary phenomena-induced stresses in heterogeneous porous media ranging from construction materials to hydrogels and living systems.

}, issn = {0027-8424}, doi = {10.1073/pnas.1901160116}, url = {http://www.pnas.org/lookup/doi/10.1073/pnas.1901160116}, author = {Zhou, Tingtao and Katerina Ioannidou and Franz-Josef Ulm and Bazant, Martin Z. and Roland Jean-Marc Pellenq} } @article {534, title = {Atomistic and mesoscale simulation of sodium and potassium adsorption in cement paste}, journal = {The Journal of Chemical Physics}, volume = {14963}, year = {2018}, month = {Aug-21-2018}, pages = {074705}, abstract = {

An atomistic and mesoscopic assessment of the effect of alkali uptake in cement paste is performed. Semi-grand canonical Monte Carlo simulations indicate that Na and K not only adsorb at the pore surface of calcium silicate hydrates (C-S-H) but also adsorb in the C-S-H hydrated interlayer up to concentrations of the order of 0.05 and 0.1 mol/kg, respectively. Sorption of alkali is favored as the Ca/Si ratio of C-S-H is reduced. Long timescale simulations using the Activation Relaxation Technique indicate that characteristic diffusion times of Na and K in the C-S-H interlayer are of the order of a few hours. At the level of individual grains, Na and K adsorption leads to a reduction of roughly 5\% of the elastic moduli and to volume expansion of about 0.25\%. Simulations using the so-called primitive model indicate that adsorption of alkali ions at the pore surface can reduce the binding between C-S-H grains by up to 6\%. Using a mesoscopic model of cement paste, the combination of individual grain swelling and changes in inter-granular cohesion was estimated to lead to overall expansive pressures of up to 4 MPa\—and typically of less than 1 MPa\—for typical alkali concentrations observed at the proximity of gel veins caused by the alkali-silica reaction.

PDF FULL TEXT

}, issn = {0021-9606}, doi = {10.1063/1.5042755}, url = {https://aip.scitation.org/doi/10.1063/1.5042755}, author = {Dufresne, Alice and Arayro, Jack and Zhou, Tingtao and Katerina Ioannidou and Franz-Josef Ulm and Roland Jean-Marc Pellenq and B{\'e}land, Laurent Karim} } @article {573, title = {Thermodynamics, kinetics, and mechanics of cesium sorption in cement paste: A multiscale assessment}, journal = {Physical Review Materials}, volume = {2}, year = {2018}, month = {May-30-2018}, chapter = {Article Number: 053608 }, abstract = {

Cesium-137 is a common radioactive byproduct found in nuclear spent fuel. Given its 30 year half life, its interactions with potential storage materials-such as cement paste-is of crucial importance. In this paper, simulations are used to establish the interaction of calcium silicate hydrates (C-S-H)-the mam binding phase of cement paste-with Cs at the nano- and mesoscale. Different C-S-H compositions are explored, including a range of Ca/Si ratios from 1.0 to 2.0. These calculations are based on a set of 150 atomistic models, which qualitatively and quantitatively reproduce a number of experimentally measured features of C-S-H-within limits intrinsic to the approximations imposed by classical molecular dynamics and the steps followed when building the models. A procedure where hydrated Ca2+ ions are swapped for Cs1+ ions shows that Cs adsorption in the C-S-H interlayer is preferred to Cs adsorption at the nanopore surface when Cs concentrations are lower than 0.19 Mol/kg. Interlayer sorption decreases as the Ca/Si ratio increases. The activation relaxation technique nouveau is used to access timescales out of the reach of traditional molecular dynamics (MD). It indicates that characteristic diffusion time for Cs1+ in the C-S-H interlayer is on the order of a few hours. Cs uptake in the interlayer has little impact on the elastic response of C-S-H. It leads to swelling of the C-S-H grams, but mesoscale calculations that access length scales out of the range of MD indicate that this leads to practically negligible expansive pressures for Cs concentrations relevant to nuclear waste repositories.

Figure

Figure

Figure

Figure

Figure

Figure

Figure

}, keywords = {CALCIUM-SILICATE-HYDRATE; C-S-H; MOLECULAR-DYNAMICS; CRYSTAL-STRUCTURE; MONTE-CARLO; IMMOBILIZATION; RADIONUCLIDES; SIMULATIONS; RELAXATION; COLLOIDS}, doi = {10.1103/PhysRevMaterials.2.053608}, url = {https://link.aps.org/doi/10.1103/PhysRevMaterials.2.053608}, author = {Arayro, Jack and Dufresne, Alice and Zhou, Tingtao and Katerina Ioannidou and Franz-Josef Ulm and Roland Jean-Marc Pellenq and B{\'e}land, Laurent Karim} }