@article {657, title = {Bilirubin oxidase-based silica macrocellular robust catalyst for on line dyes degradation}, journal = {Enzyme and Microbial Technology}, volume = {120}, year = {2019}, month = {Jan-01-2019}, pages = {77 - 83}, abstract = {

We present a new heterogeneous biocatalyst based on the grafting of Bilirubin Oxidase from Bacillus pumilus into macrocellular Si(HIPE) materials dedicated to water treatment. Due to the host intrinsic high porosity and monolithic character, on-line catalytic process is reached. We thus used this biocatalyst toward uni-axial flux decolorization of Congo Red and Remazol Brilliant Blue (RBBR) at two different pH (4 and 8.2), both in presence or absence of redox mediator. In absence of redox mediators, 40\% decolorization efficiency was reached within 24 h at pH 4 for Congo Red and 80\% for RBBR at pH 8.2 in 24 h. In presence of 10 mu M ABTS, it respectively attained 100\% efficiency after 2h and 12h. We have also demonstrated that non-toxic species were generated upon dyes decolorization. These results show that unlike laccases, this new biocatalyst exhibits excellent decolorization properties over a wide range of pH. Beyond, this enzymatic-based heterogeneous catalyst can be reused during two months being simply stored at room temperature while maintaining its decolorization efficiency. This study shows that this biocatalyst is a promising and robust candidate toward wastewater treatments, both in acidic and alkaline conditions where in the latter efficient decolorization strategies were still missing.

}, issn = {01410229}, doi = {10.1016/j.enzmictec.2018.10.004}, url = {https://linkinghub.elsevier.com/retrieve/pii/S0141022918303466}, author = {Roucher, Armand and Roussarie, Elodie and Gauvin, R{\'e}gis M. and Rouhana, Jad and Gounel, S{\'e}bastien and Stines-Chaumeil, Claire and Mano, Nicolas and Backov, Renal} } @article {673, title = {Bitumen@SiO2 core-shell particles green synthesis towards flowable powdered bitumen and their binder applications}, journal = {Colloids and Surfaces A: Physicochemical and Engineering Aspects}, volume = {570}, year = {2019}, month = {Mars-20-2019}, pages = {531 - 543}, abstract = {

Mineralization of occulated bitumen emulsions allows producing bitumen powders, also referred to as Bitumen@SiO2 hybrid particles, that can resist storage in hard conditions, with a load up to 8 kPa at 50 \°C during 20 h, without alteration of their morphology or release of their bitumen core. Thanks to the occulation, nal Bitumen@SiO2 powders are not highly pulverulent and allow transportation and handling of bitumen at ambient temperature without the need of water as it is the case for bitumen emulsions. This \“water free\” storage par- ticularity exhibits the double advantage of reducing the cost of transport and of avoiding inhibition of bitumen adhesion at mineral aggregates through the presence of water, therefore rendering the bitumen its high quality of binder. The silica shell is responsible for the high storage stability and, when mixed with aggregates for end use of asphalt, as for example in pavement applications, serves as mineral charge to the bitumen, modifying the bitumen ow properties. Indeed, when heated at 100 \°C and crushed, the capsules break releasing thus the bitumen. This suspension made of bitumen and silica shell fragments exhibits an interesting shear-thinning behavior that can be attributed to the presence of the remnant fragments. Indeed, when shell fragments have been transferred into a silicon oil, initially exhibiting a Newtonian behavior, the mixture of fragments and oil also exhibited a shear thinning rheogram demonstrating the e ect of the silica shell fragments. The bene t of such a behavior modi cation is the possibility to reduce or avoid the usual addition of llers. Passive adhesion has been tested by generating asphalt concretes with Bitumen@SiO2 powders and showed high stability.

}, issn = {09277757}, doi = {10.1016/j.colsurfa.2019.03.048}, url = {https://linkinghub.elsevier.com/retrieve/pii/S0927775719302420}, author = {Anaclet, Pauline and Depardieu, Martin and Laurichesse, Eric and Julien, Viviane and Hung, Yvong and Schmitt, Veronique and Backov, Renal} } @article {659, title = {Bulk Photodriven CO2 Conversion through TiO2@Si(HIPE) Monolithic Macrocellular Foams}, journal = {Advanced Functional Materials}, volume = {3}, year = {2019}, month = {Jan-07-2019}, pages = {1807767}, abstract = {

Operating photo-induced reactions exclusively on catalyst surfaces while not exploiting the full catalyst volume generates a major footprint penalty for the photocatalytic reactor and leads to an inefficient use of the catalytic material. Photonic investigations clearly show that the solid foams have a strongly multidiffusive character, with photons being significantly trapped within the sample cores while addressing a photon mean free path lt = 20.1 \± 1.3 \µm. This 3D process both greatly limits back-reactions and promotes outstanding selectivity toward methane (around 80\%) generation, and even ethane (around 18\%) through C-C coupling reaction, with residual carbon monoxide and dihydrogen contents (around 2\%). Silica\–titania TiO2@Si(HIPE) self-standing macrocellular catalysts lead to optimal efficient thicknesses up to 20 times those of powders, thereby enhancing the way for real 3D-photodriven catalytic processes above the millimeter scale and up to a 6 mm thickness. A rather simple Langmuir\–Hinshelwood based kinetic model is proposed which highlights the strong dependence of photocatalytic reaction rates on light scattering and the crucial role on oxidation back-reactions. In addition, a strong correlation between light attenuation coefficient and photon mean free path and median pore aperture diameter is demonstrated, offering thus a tool for photocatalytic behavior prediction.

}, doi = {10.1002/adfm.201807767}, url = {http://doi.wiley.com/10.1002/adfm.201807767}, author = {Bernadet, Sophie and Tavernier, Eug{\'e}nie and Ta, Duc-Minh and Vall{\'e}e, Renaud A. L. and Ravaine, Serge and F{\'e}cant, Antoine and Backov, Renal} } @article {594, title = {Investigation of mixed ionic/nonionic building blocks for the dual templating of macro-mesoporous silica}, journal = {Journal of Colloid and Interface Science}, volume = {533}, year = {2019}, month = {Jan-01-2019}, pages = {385 - 400}, abstract = {

Traditional porous monoliths Si(HIPE) (High Internal Phase Emulsion), prepared from the Tetradecyltrimethylammonium Bromide (TTAB)/dodecane/water system, offer high specific surface area, mainly due to microporosity. Aside, mesoporous materials SBA-15, prepared from Pluronic P123, have a high specific surface area, but are obtained as powder, which limits their applications. Starting from the mixed TTAB-P123 surfactant, it is expected to tune the mesoporosity of Si(HIPE), while keeping their monolithic character.

The ternary TTAB/P123/water phase diagram was established by varying the weight ratio between these two surfactants. The micellar structure as well as the structural parameters of the liquid crystal domains were determined by SAXS (Small Angle X-ray Scattering). The effect of dodecane solubilization was also investigated and concentrated emulsions were formulated from the (P123/TTAB)/dodecane/ water systems. After this soft matter dedicated study, the acquired knowledge was transferred toward the hierarchical porous silica generations, where the sol-gel process is involved.

Mixing P123 with TTAB, macro-mesoporous monolithic silica with an enhanced contribution of the specific surface area due to mesoporosity can be prepared. The variation of the TTAB/P123 weight ratio allows controlling the porosity at the mesoscale. Moreover, the macroporosity can be tuned by changing the preparation method, by mixing either the two micellar solutions or directly the two surfactants prior the emulsification process. (C) 2018 Elsevier Inc. All rights reserved.

}, issn = {00219797}, doi = {10.1016/j.jcis.2018.08.068}, url = {https://linkinghub.elsevier.com/retrieve/pii/S0021979718309883}, author = {Roucher, Armand and Emo, Melanie and Vibert, Francois and Stebe, Marie-Jose and Schmitt, Veronique and Jonas, Florian and Backov, Renal and Blin, Jean-Luc} } @article {660, title = {Sol{\textendash}gel process and complex fluids: sculpting porous matter at various lengths scales towards the Si(HIPE), Si(PHIPE), and SBA-15-Si(HIPE) series}, journal = {Journal of Sol-Gel Science and Technology}, volume = {18}, year = {2018}, month = {Sep-11-2018}, abstract = {

Taking inspiration from diatom hierarchically organized porosity, synthetic porous monoliths have been synthesized through rational designs while combining sol\–gel chemistry, emulsions, Pickering-based emulsions, and lyotropic mesophases. We have described the synthesis of the Si(HIPE) series employing traditional emulsions to tune the macroscopic void diameters and cationic surfactant molecules to both stabilize the oil/water interface at the macroscopic length scale and create vermicular poorly organized porosity at the mesoscopic length scale. In a second part, while substituting surfactant molecules with modified silica nanoparticles acting as emulsion-stabilizers, we depict the possibility of tuning independently the macroscopic cell diameters and the cell junctions via Pickering emulsions employed as templates, leading to the Si(PHIPE) series presenting both monodiperse macroscopic void and cell junction diameters. Finally taking the synergetic effect of nonionic surfactants and a kosmotrope salt effect we show that it is possible generating self-standing Si(HIPE) bearing high organized mesoporosity while addressing the SBA-15-Si(HIPE) series. Open image in new window Taking inspiration from diatom hierarchically organized porosity, synthetic porous self-standing silica foams have been obtained through rational designs where sol\–gel chemistry, emulsions, Pickering-based emulsions and lyotropic mesophases are advantageously combined.

}, issn = {0928-0707}, doi = {10.1007/s10971-018-4794-8}, url = {http://link.springer.com/10.1007/s10971-018-4794-8}, author = {Roucher, Armand and Schmitt, Veronique and Blin, Jean-Luc and Backov, Renal} } @article {613, title = {Inorganic, Hybridized and Living Macrocellular Foams: {\textquotedblleft}Out of the Box{\textquotedblright} Heterogeneous Catalysis}, journal = {The Chemical Record}, volume = {18}, year = {2017}, month = {Dec-01-2017}, pages = {776-787}, abstract = {

With this personal account we show how the Integrative Chemistry, when combining the sol-gel process and concentrated emulsions, allows to trigger inorganic, hybrid or living materials when dedicated toward heterogeneous catalysis applications. In here we focus on 3D-macrocellular monolithic foams bearing hierarchical porosities and applications thereof toward heterogeneous catalysis where both activities and mass transport are enhanced. We thereby first depict the general background of emulsions, focusing on concentrated ones, acting as soft templates for the design of solid (HIPE) foams, HIPE being the acronym for High Internal Phase Emulsions while encompassing both sol-gel and polymer chemistry. Secondly we extend this approach toward the design of inorganic cellular materials labeled Si(HIPE) and hybrid organic-inorganic foams, labeled Organo-Si(HIPE), where heterogeneous catalysis applications are addressed considering acidic, metallic, enzymatic and bacterial-based modified Si-HIPE. Along, we will show how the fluid hydrodynamic within the macrocellular foams is offering advanced \"out of the box\" heterogeneous catalytic capabilities.

}, keywords = {catalysts; emulsion-templating; integrative chemistry; porous matter; sol-gel process}, doi = {10.1002/tcr.v18.7-810.1002/tcr.201700075}, url = {http://doi.wiley.com/10.1002/tcr.v18.7-8}, author = {Roucher, Armand and Depardieu, Martin and Pekin, Deniz and Morvan, Micka{\"e}l and Backov, Renal} }